HDPE Waterproof Fish Pond Impervious 2.0mm Single Sided Textured Pond Liner Geomembrane

• After-sales Service: Rechargeable Installation Available
• Warranty: 10 Years
• Certification: ISO
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: HDPE-0118
• Surface: Smooth
• Application: Transportation Project, Hydraulic Project, Geotechnical Project, Environmental Project
• Feature: Puncture Resistance, Impact Resistance, Tear Resistance
• Material: HDPE
• Color: Black
• Product Name: Non-Woven Geotextile Fabric
• MOQ: Non
• Sample: Free
• Materials: 100% Polypropylene/Polyester
• Transport Package: Customization
• Specification: Customization
• Trademark: OEM
• Origin: China
• HS Code: 3920109090
• Production Capacity: 55 T/Day
• Package Size: 110.00cm * 25.00cm * 25.00cm
• Package Gross Weight: 25.000kg

Product Description

Product Description

Non-woven geotextile fabric is a synthetic permeable textile material designed to improve soil stability, provide erosion control, and aid in drainage and filtration. Typically made from polypropylene or polyester fibers, these fabrics are created through a process that involves bonding the fibers together, either thermally, chemically, or mechanically, to form a robust sheet structure.

The non-woven design of these geotextiles provides a high degree of flexibility, allowing them to conform to uneven surfaces. This makes them particularly useful in applications such as landscaping, where they can be laid beneath the soil to separate different layers and prevent the mixing of materials, like keeping gravel away from the soil in drainage systems.

Product performance	1. High anti-seepage coefficient 2. Chemical stability 3. Anti-aging performance 4. Good economic benefits 5. Construction speed is fast 6. Environmentally friendly and non-toxic
Application field	1. Environmental protection 2. Water conservancy 3. Aquaculture industry 4. Garden 5. Chemical plant, refinery 6. Mining 7. Transportation facilities 8. Agriculture 9. Subway, planting roof, sewage pipe 10. Salt film, salt pool crystallization pool
Glossy geomembrane introduction	Glossy HDPE geomembrane is a geomembrane product with a smooth surface on both sides. It is made of high quality high density polyethylene material, which is made of a combination of about 97.5% polyethylene, 2.5% carbon black, a trace amount of antioxidant and heat stabilizer. The resin used in the production process is specially designed for geomembrane. Applied raw polyethylene resin raw materials
Rough geomembrane introduction	The single-faced HDPE geomembrane is a geomembrane product that forms a matte surface by nitrogen pressure jetting on the basis of a glossy geomembrane. This process is the only way to produce a matte geomembrane without significantly reducing any of its physical properties. The geomembrane product is made of high quality high density polyethylene material, which is made of a combination of about 97.5% polyethylene, 2.5% carbon black, a trace amount of antioxidant and heat stabilizer. The resin used in the production process is designed for The raw polyethylene resin raw material actually prepared by the geomembrane application.

 

No.	index	test value
		0.75mm	1.00mm	1.25mm	1.50mm	2.00mm	2.50mm	3.00mm
1	Minimum density(g/cm²)	0.93
2	Yield Strength,N/min	11	15	18	22	29	37	44
	Breaking strength,N/min	20	27	33	40	53	67	80
	Yield elongation ratio	12
	Breaking elongation ratio	700
3	Right angle tear strength,N	93	125	156	187	249	311	374
4	Piercing strength,N	240	320	400	480	640	800	960
5	Resistant to environmental stress cracking,hr	300
6	Carbon black
	Carbon black content,%	2.0-3.0
	Carbon black dispersion	Nine of the ten observation areas should belong to Stage 1 or Stage 2, and Stage 3 should not be more than one.
7	Oxidation induction time
	Standard OIT,(min)	100
	High pressure OIT,(min)	400
8	85 baking aging(Min average)
	After baking 90d,Standard OIT %	55
	Baking 90d,High pressure OIT %	80
9	UV resistance
	Ultraviolet radiation 1600h, Standard OIT %	50
	Ultraviolet radiation 1600h, High pressure OIT %	50
10	-70 Low temperature shock enchantment performance	Pass through
11	Water vapor permeability coefficient	≤1.0*10-13
12	Dimensional stability	±2