Black Fish Tank Waterproof Membrane 1.0mm HDPE Pond Geomembrane

Product Description

Product performance	1. High anti-seepage coefficient 2. Chemical stability 3. Anti-aging performance 4. Good economic benefits 5. Construction speed is fast 6. Environmentally friendly and non-toxic
Application field	1. Environmental protection 2. Water conservancy 3. Aquaculture industry 4. Garden 5. Chemical plant, refinery 6. Mining 7. Transportation facilities 8. Agriculture 9. Subway, planting roof, sewage pipe 10. Salt film, salt pool crystallization pool
Glossy geomembrane introduction	Glossy HDPE geomembrane is a geomembrane product with a smooth surface on both sides. It is made of high quality high density polyethylene material, which is made of a combination of about 97.5% polyethylene, 2.5% carbon black, a trace amount of antioxidant and heat stabilizer. The resin used in the production process is specially designed for geomembrane. Applied raw polyethylene resin raw materials
Rough geomembrane introduction	HDPE geomembrane is a geomembrane product that forms a matte surface by nitrogen pressure jetting on the basis of a glossy geomembrane. This process is the only way to produce a matte geomembrane without significantly reducing any of its physical properties. The geomembrane product is made of high quality high density polyethylene material, which is made of a combination of about 97.5% polymer, 2.5% carbon black, a trace amount of antioxidant and heat stabilizer. The resin used in the production process is designed for The raw polyethylene resin raw material actually prepared by the geomembrane application.

 

No.	index	test value
		1.00mm	1.25mm	1.50mm	2.00mm	2.50mm	3.00mm
1	Minimum density(g/cm²)	0.93
2	Yield Strength,N/min	15	18	22	29	37	44
	Breaking strength,N/min	27	33	40	53	67	80
	Yield elongation ratio	12
	Breaking elongation ratio	700
3	Right angle tear strength,N	125	156	187	249	311	374
4	Piercing strength,N	320	400	480	640	800	960
5	Resistant to environmental stress cracking,hr	300
6	Carbon black
	Carbon black content,%	2.0-3.0
	Carbon black dispersion	Nine of the ten observation areas should belong to Stage 1 or Stage 2, and Stage 3 should not be more than one.
7	Oxidation induction time
	Standard OIT,(min)	100
	High pressure OIT,(min)	400
8	85 baking aging(Min average)
	After baking 90d,Standard OIT %	55
	Baking 90d,High pressure OIT %	80
9	UV resistance
	Ultraviolet radiation 1600h, Standard OIT %	50
	Ultraviolet radiation 1600h, High pressure OIT %	50
10	-70 Low temperature shock enchantment performance	Pass through
11	Water vapor permeability coefficient	≤1.0*10-13
12	Dimensional stability	±2